TITANIUM GRADE 4

Get a Price/Quote

Product Details:

Thickness 0.5 mm to 50 mm
Thermal Conductivity 17 W/mK
Hardness Rockwell C 2129
Tensile Strength 550 MPa min
Product Type TITANIUM GRADE 4
Types of Alloy Titanium Alloys
Material Titanium
Click to view more
Share Your Product:

Request To Call Back Send Inquiry

TITANIUM GRADE 4 Price And Quantity

Minimum Order Quantity 10 Kilograms

Standards ASTM B265, ASTM F67, UNS R50700
Applications Medical, marine, chemical processing, aerospace
Density (lb/in³) 0.163 lb/in³
Elongation 15% min
Yield Strength 485 MPa min
Surface Finish Bright, pickled, or custom
Modulus of Elasticity 105 GPa

TITANIUM GRADE 4 Product Specifications

Tensile Strength 550 MPa min
Grade GRADE 4
Product Type TITANIUM GRADE 4
Resistance Excellent corrosion resistance
Color Silver
Thickness 0.5 mm to 50 mm
Thermal Conductivity 17 W/mK
Strength High strength (highest of all commercially pure grades)
Hardness Rockwell C 2129
Chemical Composition Ti 99.2% min, Fe 0.50% max, O 0.40% max, C 0.08% max, N 0.05% max, H 0.015% max
Material Titanium
Shape Round, Square, Rectangle, Sheet, Plate, Bar, Rod
Density 4.51 Gram per cubic centimeter(g/cm3)
Types of Alloy Titanium Alloys
Melting Point Approximately 1660C

Standards ASTM B265, ASTM F67, UNS R50700
Applications Medical, marine, chemical processing, aerospace
Density (lb/in³) 0.163 lb/in³
Elongation 15% min
Yield Strength 485 MPa min
Surface Finish Bright, pickled, or custom
Modulus of Elasticity 105 GPa

TITANIUM GRADE 4 Trade Information

Supply Ability 5000 Kilograms Per Month
Delivery Time 7 Days

Product Description

Specifications:

Allvac 70
Commercially Pure Grade 4
RMI 70
Timetal 35A
Timetal 35A

Standards:

AMS: 4901
AMS: 4921
ASTM B: 265
ASTM B: 348
ASTM B: 381
ASTM F: 467 (Ti-4)
ASTM F: 468 (4)
ASTM F: 67
MIL F: 83142
MIL T: 81556
MIL T: 9046
MIL T: 9047
UNS: R50700

Chemistry Data

Carbon:0.1 max
Hydrogen:0.015 max
Iron:0.5 max
Nitrogen:0.05 max
Oxygen:0.4 max
Titanium:Balance

Physical Data

Property:Value
Density:0.163 lb/cu. in.
Specific Heat:0.129 Btu/lb/F (32-212F)
Electrical Resistivity:60 microhm-cm (at 68 F)
Melting Point:3020 F
Thermal Conductivity:9.8 (Btu/hr/ft /F)
Modulus of Elasticity (Tension):15.1 (x10 psi)
Reduction of Area:25%

Mechanical Data

Form	Sheet
Condition	Test Specimen Annealed
Temper	70
Tensile Strength	80
Yield Strength	70
Elongation	15
Reduction of Area	25

Form	Sheet
Condition	Test Specimen Annealed
Temper	600
Tensile Strength	44
Yield Strength	24
Elongation	18
Reduction of Area	75

Form	Sheet
Condition	Test Specimen Annealed
Temper	1000
Tensile Strength	27
Yield Strength	16
Elongation	29
Reduction of Area	75

Exceptional Strength and Durability

Titanium Grade 4 provides the highest strength among commercially pure titanium alloys, with a minimum yield strength of 485 MPa and tensile strength of 550 MPa. This ensures optimal performance under demanding conditions for sectors such as aerospace and medical devices, guaranteeing reliability and longevity.

Impressive Corrosion Resistance

With an excellent resistance to various corrosive environments, Titanium Grade 4 is ideal for marine, chemical, and processing applications. Its stability against oxidation and chemical attack extends product life, reducing maintenance and replacement costs.

Versatile Applications and Forms

From medical implants to marine equipment and aerospace structures, Titanium Grade 4 is engineered in multiple shapes and thicknesses. Its ease of manufacturing in sheets, plates, rods, and bars, combined with a range of custom surface finishes, provides unmatched adaptability for diverse industrial requirements.

FAQ's of TITANIUM GRADE 4:

Q: How is Titanium Grade 4 commonly processed for industrial use?

A: Titanium Grade 4 is processed through methods such as rolling, forging, and machining to produce sheets, plates, bars, and rods. These processes ensure precise control over thickness (ranging from 0.5 mm to 50 mm) and maintain the alloy's mechanical properties and surface finish as per ASTM B265 and F67 standards.

Q: What benefits does using Titanium Grade 4 provide in medical and marine applications?

A: Titanium Grade 4's superior strength, biocompatibility, and excellent corrosion resistance make it highly suitable for medical implants and marine environments. Its high purity and resistance to bodily fluids or seawater result in enhanced device longevity and reduced risk of failure.

Q: When should Titanium Grade 4 be chosen over other grades?

A: Titanium Grade 4 is preferred when maximum strength among commercially pure titanium grades is required without compromising on ductility or corrosion resistance. It is often selected for applications needing both structural integrity and exposure to aggressive environments, such as aerospace frames or chemical processing components.

Q: Where can Titanium Grade 4 materials be sourced in India?

A: Titanium Grade 4 is available from authorized dealers, distributors, manufacturers, suppliers, traders, and wholesalers throughout India. It is supplied in various shapes and sizes, tailored to specific application needs and industry standards.

Q: What standards must Titanium Grade 4 products meet?

A: All Titanium Grade 4 products should comply with industry standards such as ASTM B265, ASTM F67, and UNS R50700. These standards ensure consistent chemical composition, mechanical performance, and quality control for critical uses.

Q: How does the surface finish affect the usage of Titanium Grade 4?

A: The surface finish-bright, pickled, or custom-impacts the alloy's resistance to corrosion, ease of cleaning, and suitability for medical or chemical environments. Custom finishes can also address application-specific needs, such as increased biocompatibility or improved bonding in composite assemblies.

Tell us about your requirement

Price:

Quantity

Select Unit

50
100
200
250
500
1000+

Additional detail

Mobile number

Other Products in 'TITANIUM' category

TITANIUM GRADE 2 Minimum Order Quantity : 100 Tensile Strength : Minimum 345 MPa (50 ksi) Grade : GRADE 2 Product Type : TITANIUM GRADE 2 Strength : Moderate Strength Hardness : Other, Rockwell B70 B80 Chemical Composition : Ti: 99.2%, Fe: 0.30%, O: 0.25%, C: 0.08%, N: 0.03%, H: 0.015% Shape : Other, Round, Square, Plate, Sheet, Bar, Pipe (Various Available) Material : Titanium Color : Silver Resistance : Excellent Corrosion Resistance Thermal Conductivity : 16.4 W/mK at 20C Thickness : 0.5 mm 100 mm (customizable) Types of Alloy : Titanium Alloys Melting Point : 1665C (3029F) Density : 4.51 Gram per cubic centimeter(g/cm3)

Send Inquiry

TITANIUM GRADE 3 Minimum Order Quantity : 100 Tensile Strength : Minimum 485 MPa (70 ksi) Grade : GRADE 3 Product Type : TITANIUM GRADE 3 Strength : Higher strength than Grade 2, commercially pure Hardness : Other, Rockwell B70 B80 Chemical Composition : Ti 99.2%, Fe 0.30%, O 0.35%, C 0.08%, N 0.05%, H 0.015% Shape : Other, Bar, Rod, Sheet, Plate, Wire Material : Titanium Color : Silver Resistance : Excellent corrosion resistance Thermal Conductivity : 17.0 W/mK Thickness : 0.5 mm 40 mm (varies by product form) Types of Alloy : Titanium Alloys Melting Point : 1620 C (2950 F) Density : 4.5 Gram per cubic centimeter(g/cm3)

Send Inquiry

TITANIUM GRADE 7 Minimum Order Quantity : 100 Tensile Strength : min 345 MPa Grade : GRADE 7 Product Type : TITANIUM GRADE 7 Strength : Moderate strength Hardness : Other, Rockwell B 70 80 Chemical Composition : Titanium (Ti) balance, Palladium (Pd) 0.120.25%, Iron (Fe) 0.30%, Oxygen (O) 0.25% Shape : Other, Round Bar, Sheet, Plate, Pipe, Wire Material : Titanium Color : Silver Resistance : Outstanding corrosion resistance, especially in reducing and oxidizing environments Thermal Conductivity : 16.3 W/(mK) Thickness : 0.5 mm to 100 mm (varies as per product form) Types of Alloy : Titanium Alloys Melting Point : 1660C (3020F) Density : 4.51 Gram per cubic centimeter(g/cm3)

Send Inquiry

TITANIUM GRADE 11 Minimum Order Quantity : 10 Tensile Strength : min 379 MPa Grade : GRADE 11 Product Type : TITANIUM GRADE 11 Strength : Medium Hardness : Other, Approximately 160 HV Chemical Composition : Ti0.15Pd (Titanium with 0.15% Palladium) Shape : Other, Round Bars, Plates, Sheets, Pipes, Tubes Material : Titanium Color : Silver Resistance : Excellent corrosion resistance, especially in oxidizing and reducing environments Thermal Conductivity : 16.0 W/mK Thickness : 0.2 mm to 50 mm (typical range) Types of Alloy : Titanium Alloys Melting Point : 1665C Density : 4.51 Gram per cubic centimeter(g/cm3)

Send Inquiry

SEND INQUIRY CALL ME FREE